2024 journal article
Two new multinary chalcogenides with (Se<sub>2</sub>)<SUP>2-</SUP> dimers: Ba<sub>8</sub>Hf<sub>2</sub>Se<sub>11</sub>(Se<sub>2</sub>) and Ba<sub>9</sub>Hf<sub>3</sub>Se<sub>14</sub>(Se<sub>2</sub>)
JOURNAL OF SOLID STATE CHEMISTRY, 329.
Two multinary selenides, Ba8Hf2Se11(Se2) and Ba9Hf3Se14(Se2), with unprecedented structure types have been prepared using high-temperature synthesis techniques and represent the first known compounds in the Ba-Hf-Se system. Their structures were determined from single crystal X-ray diffraction (XRD) data. The Ba8Hf2Se11(Se2) compound crystallizes in the monoclinic C2/c space group with a = 12.3962(15) Å, b = 12.8928(15) Å, c = 18.1768(17) Å, and β = 90.685(4)°, while Ba9Hf3Se14(Se2) forms in the rhombohedral R3‾ space group with a = b = 19.4907(6) Å and c = 23.6407(11) Å. Both have pseudo-zero-dimensional structures with homoatomic Se–Se bonding in the form of (Se2)2− at distances of 2.400–2.402 Å. The structure of Ba8Hf2Se11(Se2) is comprised of [Hf2Se11]14−, Ba2+, and (Se2)2− dimers. Conversely, the Ba9Hf3Se14(Se2) structure contains a novel perovskite-type cluster constructed from eight octahedrally-coordinated Hf cations, i.e., [Hf8Se36]40−, and isolated [HfSe6]8− units which are separated by (Se2)2− dimers and Ba2+ cations. Polycrystalline Ba8Hf2Se11(Se2) is synthesized at 1073 K using a two-step solid-state synthesis method, with the co-formation of a small amount of a BaSe secondary phase. A direct bandgap of 2.2(2) eV is obtained for the polycrystalline sample of Ba8Hf2Se11(Se2), which is consistent with its yellow color. Density functional theory calculations reveal their bandgap transitions stem from predominantly filled Se-4p to empty Hf-5d at the edges of the valence bands (VB) and conduction bands (CB), respectively. The optical absorption coefficients are calculated to be relatively large, exceeding ∼105 cm−1 at about >2.0 eV with effective masses in the CB varying from ∼0.5 me (Γ → A) in Ba8Hf2Se11(Se2) to ∼1.0 me (Γ → L) in Ba9Hf3Se14(Se2). Thus, their optoelectronic properties are shown to be competitive with existing perovskite-type chalcogenides that have been a focus of recent research efforts.