Physical understanding of trends in current collapse with atomic layer deposited dielectrics in AlGaN/GaN MOS heterojunction FETs

SEMICONDUCTOR SCIENCE AND TECHNOLOGY, 31(3).

By: N. Ramanan n, B. Lee n & V. Misra n

co-author countries: United States of America 🇺🇸
author keywords: heterojunctions; power transistors; semiconductor-insulator interfaces; semiconductor device reliability; high-k gate dielectrics; atomic layer deposition; AlGaN/GaN
Source: Web Of Science
Added: August 6, 2018

Many passivation dielectrics are pursued for suppressing current collapse due to trapping/detrapping of access-region surface traps in AlGaN/GaN based metal oxide semiconductor heterojuction field effect transistors (MOS-HFETs). The suppression of current collapse can potentially be achieved either by reducing the interaction of surface traps with the gate via surface leakage current reduction, or by eliminating surface traps that can interact with the gate. But, the latter is undesirable since a high density of surface donor traps is required to sustain a high 2D electron gas density at the AlGaN/GaN heterointerface and provide a low ON-resistance. This presents a practical trade-off wherein a passivation dielectric with the optimal surface trap characteristics and minimal surface leakage is to be chosen. In this work, we compare MOS-HFETs fabricated with popular ALD gate/passivation dielectrics like SiO2, Al2O3, HfO2 and HfAlO along with an additional thick plasma-enhanced chemical vapor deposition SiO2 passivation. It is found that after annealing in N2 at 700 °C, the stack containing ALD HfAlO provides a combination of low surface leakage and a high density of shallow donor traps. Physics-based TCAD simulations confirm that this combination of properties helps quick de-trapping and minimal current collapse along with a low ON resistance.