2017 journal article

Radial growth of multi-walled carbon nanotubes in aligned sheets through cyclic carbon deposition and graphitization

CARBON, 111, 411–418.

co-author countries: United States of America 🇺🇸
Source: Web Of Science
Added: August 6, 2018

Carbon coated aligned multi-walled carbon nanotube (AMWCNT/C) sheets were used for studying the controlled radial growth of MWCNTs. Pyrolytic carbon (PyC) was deposited on the surface of nanotubes using multiple cycles of chemical vapor infiltration. Morphological and structural characterization showed that when graphitization was done in one step, after the deposition of multiple cycles of PyC, the presence of a large amount of disordered carbon on the surface of nanotubes led to a poorly graphitized coating structure that did not resembled nanotube walls anymore. Graphitization of the AMWCNT/C sheets after each deposition cycle prevented the development of disordered carbon during the subsequent PyC deposition cycles. Using the cyclic-graphitization method, thick PyC coating layers were successfully graphitized into a crystalline structure that could not be differentiated from the original nanotube walls. TEM observation and X-ray data confirmed radial growth of nanotubes, while spectra collected from Raman spectroscopy revealed that radially grown CNTs had the same quality as graphitized pristine nanotubes. The focus of this study was to compare the effect of cyclic graphitization with a one-step graphitization method to gain insight on the necessary parameters needed to radially grow high quality CNTs.