Role of Oxygen Source on Buried Interfaces in Atomic-Layer- Deposited Ferroelectric Hafnia-Zirconia Thin Films

Hsain, H. A., Lee, Y., Lancaster, S., Materano, M., Alcala, R., Xu, B., … Jones, J. L. (2022, September 7). ACS APPLIED MATERIALS & INTERFACES.

co-author countries: Germany 🇩🇪 United States of America 🇺🇸
author keywords: Hf0; 5Zr0; hafnia; zirconia; ferroelectric; orthorhombic; oxygen; texture
Source: Web Of Science
Added: September 26, 2022

Hafnia-zirconia (HfO2-ZrO2) solid solution thin films have emerged as viable candidates for electronic applications due to their compatibility with Si technology and demonstrated ferroelectricity at the nanoscale. The oxygen source in atomic layer deposition (ALD) plays a crucial role in determining the impurity concentration and phase composition of HfO2-ZrO2 within metal-ferroelectric-metal devices, notably at the Hf0.5Zr0.5O2 /TiN interface. The interface characteristics of HZO/TiN are fabricated via sequential no-atmosphere processing (SNAP) with either H2O or O2-plasma to study the influence of oxygen source on buried interfaces. Time-of-flight secondary ion mass spectrometry reveals that HZO films grown via O2-plasma promote the development of an interfacial TiOx layer at the bottom HZO/TiN interface. The presence of the TiOx layer leads to the development of 111-fiber texture in HZO as confirmed by two-dimensional X-ray diffraction (2D-XRD). Structural and chemical differences between HZO films grown via H2O or O2-plasma were found to strongly affect electrical characteristics such as permittivity, leakage current density, endurance, and switching kinetics. While HZO films grown via H2O yielded a higher remanent polarization value of 25 μC/cm2, HZO films grown via O2-plasma exhibited a comparable Pr of 21 μC/cm2 polarization and enhanced field cycling endurance limit by almost 2 orders of magnitude. Our study illustrates how oxygen sources (O2-plasma or H2O) in ALD can be a viable way to engineer the interface and properties in HZO thin films.